Composite ceramic micropermeable membrane, process and apparatus for producing such membrane

ABSTRACT

A microporous ceramic membrane comprising a porous support and a microporous layer firmly bound to each other, with a sharp geometric transition between the support and the microporous layer, the microporous layer being free of pin-holes. The microporous membrane has a predetermined average pore diameter and it is suitable for microfiltration. The membrane can comprise further microporous layers making it suitable for ultrafiltration and hyperfiltration. The membrane can be prepared by suspension coating of a support, whereby the support and/or the suspension are pretreated in order to lower temporarily the affinity between the support and the suspension.

FIELD OF THE INVENTION

The present invention relates to a microporous membrane comprising aporous ceramic support and a microporous inorganic layer. In particular,the present invention relates to an inorganic composite membranesuitable for separation and filtration of a discontinuous phase in themicrofiltration range, i.e. particles in the size range of about 20 nmto about 1 μm. Herein, "particles" do not only refer to solids but alsoto liquids (emulsion particles) or other minority components ofmulti-phase systems. Inorganic membranes have considerable advantagesover organic membranes, in that they are both chemically and thermallymore resistant.

For most purposes, a microfiltration membrane should have both highpermeability and structural strength. These requirements can in practiceonly be met by a composite membrane, wherein a macroporous supportprovides the necessary strength and a thin microporous layer, overlyingthe support, provides the microfiltration function. Such compositemembranes can be produced by coating a porous support with a microporouslayer formed out of a suspension and subsequent heating the composite.

Macroporous ceramic materials suitable as a microfiltration supportnormally exhibit structural irregularities which prevent the formationof a uniform, high performance microfilter. Coating such a support withthe microporous layer forming suspension results in partly fillingcavities in the support with microporous material and in the subsequentformation of cracks and pin-holes (apertures of the order of 10 to 100μm) in the microporous layer, by which unsatisfactory filteringproperties are obtained.

BACKGROUND OF THE INVENTION

EP-A-242,208 describes a composite membrane for ultrafiltration purposescomprising a porous inorganic support which must meet specialrequirements in that the surface has a particular pore diameter, and ispreferably of anodic aluminium oxide. These requirements make themembrane too expensive for most uses.

In EP-A-136,937, a process of producing a microporous membrane isproposed, wherein a metal oxide or metal hydroxide sol, obtained byhydrolysis of a metal compound, is thickened and acidified andsubsequently applied on a supporting layer, followed by drying andeliminating the thickening agent, and sintering. Although this processis said to prevent the formation of cracks, the complexity of theprocess is a serious drawback; furthermore, the permeability of themembrane is undesirably low.

EP-A-40,282 describes a process of producing an ultrafiltration membraneby coating a porous support, whereby the porous support is treated witha volatile liquid such as acetone or methanol, which liquid serves todraw the coating material into the pores of the support.

For the same purpose, it is known to saturate the porous support withwater prior to applying the microporous layer forming suspension.

According to EP-A-144,097, the penetration of microporous layer formingparticles into the support is prevented by reducing the contact timebetween the microporous layer forming suspension and the support.

However, the membranes obtained by these known processes are not freefrom pin-holes, if the support contains pores of more than about 5 μm.Also, the permeability of the membranes is insufficient.

OBJECTS OF THE INVENTION

Thus, it is an object of the present invention to provide a compositeceramic membrane for microfiltration purposes, having a thin, uniformmicroporous layer of the desired pore size, without pin-holes, cracks orother irregularities which damage the performance of the microfiltrationmembrane.

An object of the invention is also to provide a ceramic microporousmembrane at relatively low cost, which membrane must meet strictrequirements as to permeabilities, filtering ranges and structural andchemical integrity.

Another object of the invention is to provide a micro-filtration,ultrafiltration or hyperfiltration membrane of inorganic, compositematerials, which does not have the drawbacks of the membranes of theprior art.

Another object of the invention is to provide a process of producing acomposite microporous membrane. Another object of the invention is toprovide an apparatus for applying a coating suspension onto a tubularporous support.

SUMMARY OF THE INVENTION

The invention has the following features:

the microporous layer is firmly bound to the geometric outer surface ofthe porous support, making the membrane structurally stable and suitablefor multiple regeneration by applying high back flush pressures, ifnecessary;

the microstructural transition between the porous support and themicroporous layer is very sharp, the packing of the particles being suchthat the support material and the microporous layer material do notinterfere with each other's permeabilities;

the microporous layer is thin and has a smooth outer surface, resultingin a high and uniform permeability;

the microporous layer has a predetermined average pore diameter,depending on the intended use, and it has a narrow pore diameterdistribution; in particular, the diameter distribution is sharplyconfined with respect to larger pore diameters than the average, forexample, 99% of the pore volume consists of pores with a diameter ofless than 1:15 times the average diameter, and 99.9% of the pore volumeconsists of pores with a diameter of less than 1.2 times the averagediameter;

the microporous layer is free of pin-holes and other structuralirregularities which would seriously impair the separation performancesof the membrane;

the inner face of the microporous layer closely follows the surface ofthe porous support in such a way that pores in the support having aneven greater diameter than the thickness of the microporous layer arespanned by the microporous layer;

the membrane has a high permeability.

The thickness of the microporous layer can be chosen according to theintended use of the membrane. It is typically between 10 and 100/μm andpreferably between 15 and 30 μm. The average pore size of themicroporous layer can have any value in the microfiltration range i.e.about 20 nm to 1 μm. It is preferably between 100 and 500 nm; Themicroporous layer consists preferably of at least one metal oxide suchas aluminium oxide, titanium oxide, zirconium oxide, yttrium oxide,silicon oxide etc. More preferably it consists essentially of aluminiumoxide.

The porous support can have any thickness, e.g. between 500 μm and 1 cmand more, provided that it has sufficient structural strength. It canhave pore sizes between 0.1 μm and 50 μm or even greater.

The porous support can be of any ceramic material such as oxides ofaluminium, silicon, titanium and other metals, and mixtures thereof,possibly together with oxides of other elements such as alkali, alkalineearth, and earth metals etc.; other materials such as metals, glass,carbon can also be used as a support. In a preferred embodiment, theporous support consists mainly of sintered alpha alumina.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 schematically shows a cross-section of a typical membrane of theinvention.

FIG. 2 is a graph illustrating the relationship between the withdrawalrate and the coating thickness;

FIG. 3 is a schematic illustration of one embodiment of an apparatus forcoating a tubular support with a coating suspension;

FIG. 4 is a schematic illustration of an alternative embodiment of theapparatus of FIG. 3;

FIG. 5 is a schematic illustration of another alternative embodiment ofthe apparatus for internally coating a tubular substrate.

DETAILED DESCRIPTION OF THE INVENTION

The membrane of the invention can have any shape such as a tube, plate,cup, funnel etc., and size, which are suitable for the intendedseparation process.

The present invention also relates to a microporous membrane consistingof a composite membrane as described hereabove and one or moresubsequent microporous layers bound to the first microporous layer, atleast one and preferably each subsequent layer having a lower averagepore diameter than the preceding layer. Such three-layer or multilayermembranes are especially useful, when the desired pore size cannotsatisfactorily be achieved with a two component membrane, for examplewhen the desired pore size is below 20 nm. Because of the smooth surfaceof the microfiltration layer, the second and possible further layers canbe very thin, e.g. 1 μm-10 μm, and have pores in the range of 0.5-100nm, in particular 0.5-20 nm, thus providing a microfiltration, or,especially, an ultrafiltration or hyperfiltration membrane having asharp filtration range and relatively high permeability.

The present invention also relates to a process for producing amicroporous membrane, such as the microfiltration membrane referred toabove, wherein a porous ceramic support is coated with a microporouslayer forming suspension and the coated support is heated.

The process is characterized in that, before coating the support, theaffinity between the porous support and the microporous layer formingsuspension is lowered such that penetration of the suspension into theinternal structure of the porous support is substantially prevented,while wetting of the surface of the porous support during coating is notprevented.

In the process of the invention, the suspended particles of themicroporous layer forming suspension cannot easily enter cavitiessituated in the porous support, which would otherwise result in theformation of pin-holes and cracks in the microporous layer upon dryingthe membrane. Pore sizes up to 50 μm of the porous support do not resultin such pin-holes, when the process of the invention is used. This meansthat relatively low grade, and therefore inexpensive, materials can beused in the present process to produce a microfiltration membrane withexcellent separation characteristics.

The affinity between the porous support and the coating suspension canbe measured for example by means of the contact angle, i.e. the internalangle of the edge between droplets of the suspension and the geometricsupport surface. On measuring the contact angle, the dimensions of thedroplets should be significantly greater than the surface pore diameter.A small angle, down to 0°, corresponds to perfect wetting, whereas alarge angle, up to 180° corresponds to non wetting. For example thecontact angle between a ceramic support and an aqueous suspension isnormally between 30°-60°. In the process of the invention, the affinitybetween the support and the suspension is lowered such that the contactangle is greater than 60°, preferably between 75° and 135° and morepreferably between 90° and 120°.

The affinity between the support and the suspension can be altered byaltering the hydrophilicity of the support and/or the suspension.Preferably, the affinity is lowered by lowering the hydrophilicity ofthe porous support, in other words, by making the support morehydrophobic. This can be done, e.g. by converting hydroxy groups and oxygroups on the surface of the ceramic support into less hydrophilicgroups such as esters, ethers and the like. Lowering of the affinity ofthe support for the coating suspension does not affect the adherence ofthe microporous layer to the support after drying.

In a preferred embodiment, the porous support is made more hydrophobicby treating it with a silane composition, i.e. an undiluted or,preferably, diluted silane compound. Such a silane compound containsrelatively hydrophobic groups, such as alkyl groups, substituted alkylgroups, alkenyl groups, phenyl groups, alkoxy groups, acyloxy groups,etc. It also contains groups, such as hydroxy groups, alkoxy groups,halogens etc., which can react, directly or indirectly, with reactivegroups present on the support surface. Silanes which are very useful inthe process of the invention are trialkoxy-alkylsilanes, for exampletrimethoxymethylsilane, dialkoxy-phenyl-alkylsilanes,triacyloxy-alkylsilanes or trialkoxy substituted alkyl-, such ashydroxyalkyl- or aminoalkyl-silanes and the like. An alkoxy group canreact with hydroxy groups present on the support surface, directly, orafter hydrolysis to a hydroxy group, thus lowering the hydrophilicity ofthe support surface.

The degree of lowering of the hydrophilicity can be controlled byvarying the amount and/or the concentration of the silane compositionwith which the support is treated, and by the treatment length andtemperature. Preferably, the duration of the treatment is long enough toallow the silane composition to penetrate the pores of the poroussupport.

Advantageously, the silane composition contains a solvent which can beeasily removed after the treatment. Examples of suitable solvents arelower ketones, such as acetone, methylethyl ketone, etc., loweralcohols, such as methanol, ethanol, etc., and lower ethers, such asdiethyl ether, tetrahydrofuran, dioxane, etc. The solvent can be removedby evaporation at ambient or elevated temperature, for example between15° C. and 105° C., depending on the particular solvent.

The concentration of the silane solution is not limiting, 0.1-10% is auseful concentration range; preferably, the concentration is between 0.5and 5% by weight.

Silane compositions are often referred to as "silane primers" or "silanecoupling agents". Such compositions can be used in the present process.

Silanes suitable for use in the process of the invention arecommercially available, for example, Dow Corning® Z-6020, Z-6030 andZ-6070, or Silane PC₁₂ from Permacol B.V.. The silane composition maycontain other ingredients such as cosolvents, stabilisers, hydrolysiscatalysts etc..

In order to accelerate the hydrophilicity lowering process and to adjustthe desired hydrophilicity, it has been found to be of advantage toexpose the silane treated support to small amounts of water. This can bedone by evaporating the solvent in the presence of moist air, or byusing a solvent, such as a ketone, which contains a small amount ofwater. Depending on the amount of water present and on the desiredhydrophilicity, the preferred time interval between the silanepretreatment and the coating with the microporous layer formingsuspension, can be chosen, for example from 30 to 60 minutes.

Preferably, the treatment with the silane composition results in amonolayer of silicon containing groups. For example, infrared analysisshows that, after treatment with trimethoxy-methylsilane,hydroxy-methoxy-methylsilyloxy groups are present on the support.Assuming a mean surface area per silyl group of 1 nm², 10 mg oftrimethoxymethylsilane produces a monolayer of about 40 m². This meansthat 1 liter of a 1% silane solution is sufficient for pretreating asupport having an effective surface area of 40 m².

The treatment with a silane composition can be effected by simplyimmersing the support in the silane composition, or by spraying,rinsing, brushing or any other convenient method. Preferably, immersionis carried out slowly enough to allow the silane composition to beabsorbed in the pores of the support.

The treatment with the silane composition results into a morehydrophobic internal surface of the porous support. Thus, upon coatingthe pretreated support, large pores of the support are spanned by themicroporous layer rather than filled up with microporous suspensionparticles.

However, the outer surface of the support should still have sufficientaffinity for the coating suspension, in order to create a strong bondbetween the porous support and the microporous layer. This can beeffected by adjusting the hydrophilicity of either of the components.

In the heating step after the pretreated support is coated with themicroporous layer forming suspension, the silane groups are partiallyevaporated, and partially converted into silicon dioxide. According toX-ray analysis, the residue after heating is amorphous; the SiO₂ contentappeared to be 98%.

The microporous layer forming suspension to be used in the process ofthe invention is preferably an aqueous suspension of a metal oxide orhydroxide or of a precursor thereof, such as a metal alkoxide. Suitablemetals for said metal oxides, hydroxides and alkoxides are group III,IV, V, VI, VII and VIII metals, such as aluminium, titanium, zirconium,yttrium, silicon, manganese etc. Aluminium oxide appears to beparticularly useful, in that it is relatively inexpensive and can besupplied in various grades and sizes. The particle size can be chosenaccording to the desired pore size of the microporous membrane. Ingeneral, particle sizes between for example 10 nm and 1 μm are suitable.

Instead of lowering the affinity between the support and the suspensionby lowering the hydrophilicity of the support, the affinity can belowered by lowering the hydrophilicity of the aqueous suspension, e.g.by making it less polar.

If the affinity has been adjusted by silane treatment, as describedabove, a further adjustment in affinity can be made by adding adetergent to the aqueous suspension, making the affinity between thesupport and the suspension higher again, inducing an attractiveinteraction between the porous support and the microporous layer, whileat the same time the pores of the support are not penetrated excessivelywith suspended particles.

The microporous layer forming suspension can be applied by immersing thesupport in the suspension, or by spraying or other conventional methods.According to the invention, the suspension is preferably applied byimmersion.

The thickness of the microporous layer can conveniently be controlled byvarying the speed of withdrawing the immersed porous support from thecoating suspension. For example, a support immersed in a 37.5% by weightAl₂ O₃ suspension is coated with a microporous layer of 20 μm afterdrying, when it is removed at a rate of 2.5 mm/s, whereas a microporouslayer of 50 μm after drying results when the rate of removal from thecoating suspension is 20 mm/s. The relationship between the withdrawalrate and the coating thickness is graphically illustrated in FIG. 2,wherein the abscissa represents the withdrawal rate and the ordinaterepresents the thickness of the microporous layer after drying.

In contrast, the duration of contact between the porous support and thecoating suspension has little effect on the thickness of the microporouslayer.

The thickness of the microporous layer can be increased, if desired, bycarrying out two or more coating steps, with intermittent partial orcomplete drying.

It can be of advantage to carry out two or more coating steps, withsuspensions having decreasing particle sizes. In this way, a microporousmembrane with smaller pore size, for example in the ultrafiltration oreven hyperfiltration range, is obtained. Such a second and furthermicroporous layer with reduced pore size can conveniently be appliedusing a sol-gel process, for example as described in EP-A-144,097.

The pore size, the porosity and the permeability of the microporouslayer can be adjusted by varying the sintering temperature of the coatedmembrane, and by varying the particle size and the type of suspendedparticles.

Typically, the pore size of a two component microfiltration membrane canbe selected between 20 nm and 1 μm, the porosity can be between 30 and70% and the liquid permeability is between 100 and 20,000 1 /h.m².bar.

The invention also relates to an apparatus for coating a tubular supportwith a coating suspension, wherein the support can be removed from thesuspension or vice versa at a determined rate. Such an apparatus canalso be used for applying a second and further layer by a sol-gelprocess.

The apparatus of the invention comprises a collar fitting into or arounda tubular substrate, and means for axially moving the tubular substratewith respect to the collar at a controlled rate, which collar can carrya coating suspension, optionally fed from a storage tank.

FIGS. 3 and 4 illustrate such apparatus.

FIG. 3 shows an apparatus for internally coating a tubular substrate 1,which substrate is fixed by holders 2 and 3 joined to (a part of) adevice 4, which is capable of vertically moving the tube 1 with theholders 2 and 3 at a defined rate.

A sealing collar 5 is located inside the tube 1 against the interiorwall. The collar is fixed to the apparatus, i.e. it can move withrespect to the tube. The space above collar 5 is connected to a storagetank 6, by conducts 7, 7' and 7" and optionally a pump 8. The storagetank 6 is equipped with a stirring device 9 for keeping the suspensionin the tank homogeneous.

Upon moving upward the tubular substrate 1 with the holders 2 and 3, thesuspension level 11 is withdrawn downwards along the interior of atubular substrate 1, and a layer 12 of the coating suspension adheres tothe substrate. The thickness of this layer 12 depends on the rate ofmoving of the substrate with respect to the collar 5. Thus, the entireinterior of the tube 1 is coated with a layer 12.

FIG. 4 shows a similar apparatus for externally coating a tubularsubstrate 1. Two sealing collars 21 and 22, suitably spaced apart,together with fixing means 23 and 23', form a closed space. This spaceis connected to a suspension containing tank 25, which suspension can befed through pump 26 and conducts 27, 27' and 28. The tubular substrate 1is fixed by a support 28' which is joined to a means 29 for verticallymoving the tube. Thus, the entire exterior of the tube 1 can be coatedwith a layer 30.

FIG. 5 shows another apparatus for internally coating a tubularsubstrate 1, which is especially useful for coating tubes having smallinternal diameters. Tube 1 can be held in a fixed position by a support31 and is connected by a flexible conduct 32 with a vessel 33 containingthe coating suspension. The vessel is capable of moving verticallydownwards with respect to the tube 1, whereby the coating suspension iswithdrawn downwards from the tube at a corresponding rate.Alternatively, the vessel 33 is held in a fixed position and the tube 1with support 31 can be moved upward.

The invention is further illustrated with the following nonlimitingexamples.

EXAMPLE 1

A tube having an external diameter of 20 mm and a wall thickness of 3mm, consisting of a mixture of sintered alpha alumina and mullite havinga pore size range between 0.1 μm and 5 μm and an average pore radius of1 μm (determined by mercury porosimetry) with large surface pores of upto 50 μm (observed by electron microscopy), was slowly immersed into a1% silane solution (Silane PC₁₂ from Permacol B.V., Holland) in acetone,for 10 minutes, allowing all pores of the tubular support to be filledwith the solution. Then, the tube was taken from the solution and driedin the air at 50° C., until constant weight.

Then, the pretreated and dried tube was vertically coated with amicropermeable layer forming suspension consisting of 100 g Al₂ O₃,grade Alcoa (A16SG), ground to 0.25 μm particles and dispersed in 140 gof demineralized water, using an apparatus as illustrated in FIG. 3 orFIG. 4. The tube was coated with a withdrawal rate of 5 mm/s. Theadhering coating was 20 μm thick and the porosity after heating at 1200°C. for 2 hours was 38%. No pinholes could be detected in themicrofiltration layer by electron microscopy. The permeability of thecomposite membrane thus produced was 700 1 /h.m².bar. The average poreradius of the microfiltration layer was 0.06 μm.

EXAMPLE 2

A tube having an external diameter of 20 mm and a wall thickness of 2.5mm, consisting of sintered alpha alumina having an average pore radiusof 1.5 μm (determined by mercury porosimetry) with large surface poresof up to 20 μm (observed by electron microscopy), was slowly immersedinto a 1% silane solution (Silane PC₁₂ from Permacol B.V., Holland) inacetone, for 10 minutes allowing all pores of the tubular support to befilled with the solution. Then the tube was taken from the solution anddried in the air at 50° C., until constant weight.

Then the pretreated and dried tube was vertically coated with amicropermeable layer forming suspension, consisting of 100 g Al₂ O₃,grade Baikalox CR6, ground and dispersed in 140 g of demineralizedwater, using an apparatus as illustrated in FIG. 3. The tube was coatedwith a withdrawal rate of 5 mm/s. The adhering coating was 30 μm thickand the porosity after heating at 1200° C. for 2 hours was 54%. Nopin-holes or microcracks could be detected in the microfiltration layerby electron microscopy. The permeability of the composite membrane thusproduced was 8500 1 /h.m².bar. The average pore radius of themicrofiltration layer was 0.12 μm.

EXAMPLE 3

The two-layer membrane (substrate+microfiltration layer) obtainedaccording to Example 2 was subsequently coated with a boehmite sol usingthe apparatus of FIG. 3. The boehmite sol (0.7 mol/l) was peptized withnitric acid (molar ratio HN0₃ /boehmite of 0.1) and contained 1% byweight of glycerol. The coating was then dried under laboratoryconditions and sintered at 600° C. during 5 hours. The thickness of thetop layer thus obtained was 2 μm. The layer was smooth and contained nopin-holes or cracks (examined by electron microscopy). The pores of thelayer had an average size of about 2 nm with a narrow distribution.Thus, an excellent, three-component ultrafiltration membrane wasobtained.

We claim:
 1. A two layer microporous membrane consisting of a porousceramic support having pore sizes between 0.1 μm and 50 μm and only onemicroporous sintered inorganic layer, wherein the microporous layer isbonded directly to the geometric outer surface of the porous support,thereby substantially spanning the pores of the support, with a sharptransition in permeability between the microporous layer and the poroussupport, the microporous layer having a predetermined average porediameter between 20 nm and 1 μm, and being essentially free ofpin-holes.
 2. The membrane of claim 1, characterized by a thickness ofthe microporous layer of 10-100 μm, preferably 15-30 μm.
 3. The membraneof claim 1, characterized by an average pore diameter of the microporouslayer of 100-500 nm.
 4. The membrane of claim 1, characterized in thatthe microporous layer consists essentially of a metal oxide.
 5. Themembrane of claim 4, characterized in that the metal oxide is alumina.6. The membrane of claim 1, characterized in that the porous supportconsists essentially of alpha alumina.